Electrical Transport — Enhancing pancreatic cancer ablation efficiency: bipolar IRE with conductive MOF

Measurement evidence

Electrical Transport

Enhancing pancreatic cancer ablation efficiency: bipolar IRE with conductive MOF · Xu L., Lou W., Xu F. et al. · Materials Chemistry Frontiers · 2025 · 2018-2030

2 measurement groups · 8 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Solution conductivity measurement

Electrical conductivity

Ni3(HITP)2@PDA nanoparticles · Powder

Conductivity of Ni3(HITP)2@PDA aqueous dispersions at increasing concentration, read from Fig. 2i.

Atmosphere
aqueous solution
Geometry
solution conductivity
Context
Composite sample.
Measurement source
2023 · 3.3 Characterization of conductive MOF · Fig. 2i
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
Ni3(HITP)2@PDA conductivity at 0 ug/mLapproximately 1 uS/cm from Fig. 2i——Figure Axis
Approximate		2023 · 3.3 Characterization of conductive MOF · Fig. 2i
Ni3(HITP)2@PDA conductivity at 1000 ug/mLMarked as a best value within this paperapproximately 58 uS/cm from Fig. 2i——Figure Axis
Approximate		2023 · 3.3 Characterization of conductive MOF · Fig. 2i
Ni3(HITP)2@PDA conductivity at 125 ug/mLapproximately 7 uS/cm from Fig. 2i——Figure Axis
Approximate		2023 · 3.3 Characterization of conductive MOF · Fig. 2i
Ni3(HITP)2@PDA conductivity at 250 ug/mLapproximately 15 uS/cm from Fig. 2i——Figure Axis
Approximate		2023 · 3.3 Characterization of conductive MOF · Fig. 2i
Ni3(HITP)2@PDA conductivity at 500 ug/mLapproximately 31 uS/cm from Fig. 2i——Figure Axis
Approximate		2023 · 3.3 Characterization of conductive MOF · Fig. 2i

Solution conductivity measurement

Electrical conductivity

Purchased Ni3(HITP)2 powder · Powder

Conductivity of aqueous dispersions of Ni3(HITP)2 and Ni3(HITP)2@PDA at 0-1000 ug/mL, read from SI Fig. S14.

Atmosphere
aqueous solution
Geometry
solution conductivity
Context
Pristine MOF control compared with PDA-coated composite.
Measurement source
p015 · Supporting Information · Fig. S14
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
Conductivity retained after PDA modificationNi3(HITP)2 retained its conductive properties following PDA modification——Text
Qualitative		2023 · 3.3 Characterization of conductive MOF · Fig. S14
Ni3(HITP)2@PDA conductivity at 1000 ug/mLMarked as a best value within this paperapproximately 59 uS/cm from Fig. S14——Figure Axis
Approximate		p015 · Supporting Information · Fig. S14
Ni3(HITP)2 conductivity at 1000 ug/mLMarked as a best value within this paperapproximately 58 uS/cm from Fig. S14——Figure Axis
Approximate		p015 · Supporting Information · Fig. S14