Porosity — High-mobility band-like charge transport in a semiconducting two-dimensional metal–organic framework

Measurement evidence

Porosity

High-mobility band-like charge transport in a semiconducting two-dimensional metal–organic framework · Dong R., Han P., Arora H. et al. · Nature Materials · 2018 · 1027-1032

1 measurement group · 1 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

N2 sorption isotherm and BET surface area analysis

Gas sorption and porosity

Large-area free-standing Fe3(THT)2(NH4)3 multilayer film · Thin Film

N2 sorption measured at 77 K; samples degassed at 120 C for at least 4 h.

Temperature: 77
Atmosphere: N2
Geometry: MOF film powder/film sample for sorption
Context: pristine framework
Measurement source: SI p.8/44 · Structural characterization · Fig. S4

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET specific surface areaMarked as a best value within this paper	526 +/- 5 m2 g-1	—	+/- 5 m2 g-1	Caption Exact Reported	SI p.8/44 · Structural characterization · Fig. S4