Tuning the Structure-Property Relationships of Metallophthalocyanine-Based Two-Dimensional Conductive Metal-Organic Frameworks with Different Metal Linkages · Noh H.-J., Cline E., Pennington D.L. et al. · Journal of the American Chemical Society · 2025 · 8240-8249
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
CuPc-O-Cu black powder · Powder
N2 isotherms measured at 77 K after degassing under vacuum at 100 deg C for 18 h.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| N2 isotherm type | type 2 characteristic; microporosity/pseudo-columnar pores | — | — | Text Qualitative | main p.6 · Results and Discussion · Figure S22 |
| BET surface area | 447.9 m2 g-1 | — | — | Text Exact Reported | main p.6 · Results and Discussion · Figure S22 |
CuPc-O-Ni black powder · Powder
N2 isotherms measured at 77 K after degassing under vacuum at 100 deg C for 18 h.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| N2 isotherm type | type 2 characteristic; microporosity/pseudo-columnar pores | — | — | Text Qualitative | main p.6 · Results and Discussion · Figure S22 |
| BET surface area | 476.9 m2 g-1 | — | — | Text Exact Reported | main p.6 · Results and Discussion · Figure S22 |
CuPc-O-Zn black powder · Powder
N2 isotherms measured at 77 K after degassing under vacuum at 100 deg C for 18 h.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| N2 isotherm type | type 2 characteristic; microporosity/pseudo-columnar pores | — | — | Text Qualitative | main p.6 · Results and Discussion · Figure S22 |
| BET surface area | 460.0 m2 g-1 | — | — | Text Exact Reported | main p.6 · Results and Discussion · Figure S22 |