Other — 2D Semiconducting Metal–Organic Framework Thin Films for Organic Spin Valves

Measurement evidence

Other

2D Semiconducting Metal–Organic Framework Thin Films for Organic Spin Valves · Song X., Wang X., Li Y. et al. · Angewandte Chemie - International Edition · 2020 · 1118-1123

1 measurement group · 3 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Magnetic hysteresis loop measurement (SQUID-VSM)

Magnetometry and magnetic susceptibility

LSMO/Cu3(HHTP)2(100 nm)/Co/Au organic spin valve · Electrode

M-H curves compared for LSMO/2D c-MOF/Co device and individual LSMO electrode at 10 K; Cu3(HHTP)2 film measured at 100 K.

Temperature: 10; 100
Geometry: OSV stack and film controls
Context: device magnetic switching and pristine MOF nonferromagnetic control
Measurement source: 1120 · Results and Discussion · Figure 4c; Figures S14-S15

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
high coercivity attributed to Co layer	180 Oe at 10 K	—	—	Text Exact Reported	1120 · Results and Discussion · Figure 4c; Figure S15
low coercive field attributed to LSMO	around 60 Oe at 10 K	—	—	Text Approximate	1120 · Results and Discussion · Figure 4c; Figure S14a
Cu3(HHTP)2 film magnetic behaviour	nonferromagnetic at 100 K	—	—	Qualitative Qualitative	1120 · Results and Discussion · Figure S15