Electrical Transport — Ultrafast in Situ Synthesis of Large-Area Conductive Metal-Organic Frameworks on Substrates for Flexible Chemiresistive Sensing

Measurement evidence

Electrical Transport

Ultrafast in Situ Synthesis of Large-Area Conductive Metal-Organic Frameworks on Substrates for Flexible Chemiresistive Sensing · Chen X., Lu Y., Dong J. et al. · ACS Applied Materials and Interfaces · 2020 · 57235-57244

1 measurement group · 9 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Four-electrode conductivity

Electrical conductivity

Cu-BHT film reaction-time series · Thin Film

Conductivity versus reaction time at room temperature

Atmosphere: ambient
Geometry: thin film; four-electrode method
Context: pristine Cu-BHT films
Measurement source: p004; article page 57238 · 3.2 Characterization · Figure S5a

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Conductivity at 10 min reaction time	1500 S/cm	—	—	Figure Axis Approximate	p006 · Figure S5 · Figure S5a
Conductivity at 12 min reaction time	1515 S/cm	—	—	Figure Axis Approximate	p006 · Figure S5 · Figure S5a
Conductivity at 14 min reaction timeMarked as a best value within this paper	1532 S/cm	—	—	Text Rounded Reported	p004; article page 57238 · 3.2 Characterization · Figure S5a
Conductivity at 16 min reaction time	1530 S/cm	—	—	Figure Axis Approximate	p006 · Figure S5 · Figure S5a
Conductivity at 2 min reaction time	1190 S/cm	—	—	Figure Axis Approximate	p006 · Figure S5 · Figure S5a
Conductivity at 4 min reaction time	1320 S/cm	—	—	Figure Axis Approximate	p006 · Figure S5 · Figure S5a
Conductivity at 5 s reaction time	1005 S/cm	—	—	Text Rounded Reported	p004; article page 57238 · 3.2 Characterization · Figure S5a
Conductivity at 6 min reaction time	1420 S/cm	—	—	Figure Axis Approximate	p006 · Figure S5 · Figure S5a
Conductivity at 8 min reaction time	1485 S/cm	—	—	Figure Axis Approximate	p006 · Figure S5 · Figure S5a