Sensing Application — Ultrafast in Situ Synthesis of Large-Area Conductive Metal-Organic Frameworks on Substrates for Flexible Chemiresistive Sensing

5 measurement groups · 25 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Flexible NH3 sensing under bending

Flexible Cu-BHT chemiresistor sensor on PET/Au electrodes · Electrode

20 ppm NH3; bending radii flat, 10, 7 and 3 mm; 1000 cycles at 3 mm

Atmosphere: air
Geometry: PET/Au flexible sensor
Context: pristine Cu-BHT active film
Measurement source: p006; article page 57240 · 3.4 Mechanical Stability · Figure 4

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Bending-cycle enduranceMarked as a best value within this paper	1000 cycles at 3 mm bending radius with slight response change	—	—	Text Exact Reported	p006; article page 57240 · 3.4 Mechanical Stability · Figure 4d
Bending radii tested	flat, 10, 7 and 3 mm	—	—	Text Range	p006; article page 57240 · 3.4 Mechanical Stability · Figure 4b,c
20 ppm NH3 response at 3 mm bending radius	about 7.4%	—	—	Figure Axis Approximate	p006; article page 57240 · 3.4 Mechanical Stability · Figure 4c
20 ppm NH3 response under flat bending state	about 6.9%	—	—	Figure Axis Approximate	p006; article page 57240 · 3.4 Mechanical Stability · Figure 4c

Humidity-dependent NH3 sensing

Cu-BHT-2 min chemiresistor sensor on Si/SiO2/Au interdigitated electrodes · Electrode

20 ppm NH3 under 0-80% relative humidity

Atmosphere: humidified air
Geometry: Si/SiO2/Au sensor
Context: pristine Cu-BHT active film
Measurement source: p005; article page 57239 · 3.3 Gas-Sensing Performance · Figure S7

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Response at 0% RH	-7.88%	—	—	Text Exact Reported	p005; article page 57239 · 3.3 Gas-Sensing Performance · Figure S7
Response at 80% RH	-4.01%	—	—	Text Exact Reported	p005; article page 57239 · 3.3 Gas-Sensing Performance · Figure S7

Chemiresistive NH3 sensing

Cu-BHT-2 min chemiresistor sensor on Si/SiO2/Au interdigitated electrodes · Electrode

Room temperature; NH3 1-100 ppm; 0.01 V across 200 um x 2000 um interdigitated electrodes

Atmosphere: air/dry gas
Geometry: Si/SiO2 with Cr/Au interdigitated electrodes
Context: pristine Cu-BHT active film
Measurement source: p005; article page 57239 · 3.3 Gas-Sensing Performance · Figure 3

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Log-log response-concentration R2	R2 = 0.99	—	—	Figure Axis Rounded Reported	p005; article page 57239 · 3.3 Gas-Sensing Performance · Figure 3
Log-log response-concentration fit slope	y = 0.68x - 0.08	—	—	Figure Axis Rounded Reported	p005; article page 57239 · 3.3 Gas-Sensing Performance · Figure 3
NH3 detection range	1-100 ppm	—	—	Text Range	p005; article page 57239 · 3.3 Gas-Sensing Performance · Figure 3/Table S1
NH3 limit of detectionMarked as a best value within this paper	0.23 ppm	—	—	Text Exact Reported	p005; article page 57239 · 3.3 Gas-Sensing Performance · Figure 3/Table S1
Recovery time after 20 ppm NH3	102 s	—	—	Text Exact Reported	p005; article page 57239 · 3.3 Gas-Sensing Performance · Figure 3/Table S1
Repeatability coefficient of variation	0.145%	—	—	Text Exact Reported	p005; article page 57239 · 3.3 Gas-Sensing Performance · Figure 3/Table S1
Response to 20 ppm NH3 for Cu-BHT-10 min	2.3%	—	—	Figure Axis Approximate	p006-p007; article pages 57240-57241 · 3.5 Sensing Mechanism · Figure 5a
Response to 20 ppm NH3 for Cu-BHT-12 min	1.9%	—	—	Figure Axis Approximate	p006-p007; article pages 57240-57241 · 3.5 Sensing Mechanism · Figure 5a
Response to 20 ppm NH3 for Cu-BHT-14 min	1.77%	—	—	Text Exact Reported	p006-p007; article pages 57240-57241 · 3.5 Sensing Mechanism · Figure 5a
Response to 20 ppm NH3 for Cu-BHT-2 minMarked as a best value within this paper	7.02%	—	—	Text Exact Reported	p006-p007; article pages 57240-57241 · 3.5 Sensing Mechanism · Figure 5a
Response to 20 ppm NH3 for Cu-BHT-4 min	5.8%	—	—	Figure Axis Approximate	p006-p007; article pages 57240-57241 · 3.5 Sensing Mechanism · Figure 5a
Response to 20 ppm NH3 for Cu-BHT-5 s	5.08%	—	—	Text Exact Reported	p006-p007; article pages 57240-57241 · 3.5 Sensing Mechanism · Figure 5a
Response to 20 ppm NH3 for Cu-BHT-6 min	4.8%	—	—	Figure Axis Approximate	p006-p007; article pages 57240-57241 · 3.5 Sensing Mechanism · Figure 5a
Response to 20 ppm NH3 for Cu-BHT-8 min	3.5%	—	—	Figure Axis Approximate	p006-p007; article pages 57240-57241 · 3.5 Sensing Mechanism · Figure 5a
Response time to 20 ppm NH3	58 s	—	—	Text Exact Reported	p005; article page 57239 · 3.3 Gas-Sensing Performance · Figure 3/Table S1
Driving voltageMarked as a best value within this paper	0.01 V	—	—	Text Exact Reported	p005; article page 57239 · 3.3 Gas-Sensing Performance · Figure 3/Table S1

Chemiresistive selectivity test

Cu-BHT-2 min chemiresistor sensor on Si/SiO2/Au interdigitated electrodes · Electrode

100 ppm acetone, toluene, THF, DMC, hexane, ethanol, H2O, ethyl acetate and NH3

Atmosphere: air
Geometry: Si/SiO2/Au sensor
Context: pristine Cu-BHT active film
Measurement source: p005; article page 57239 · 3.3 Gas-Sensing Performance · Figure 3f

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
NH3 selectivity value rangeMarked as a best value within this paper	30-50	—	—	Text Range	p005; article page 57239 · 3.3 Gas-Sensing Performance · Figure 3f
NH3 selectivity value in comparison tableMarked as a best value within this paper	30	—	—	SI Table Exact Reported	p008 · Table S1 · Table S1

Long-term ambient stability and repeatability

Cu-BHT-2 min chemiresistor sensor on Si/SiO2/Au interdigitated electrodes · Electrode

20 ppm NH3 repeatability; ambient-air storage up to 2 months

Atmosphere: ambient air
Geometry: Si/SiO2/Au sensor
Context: pristine Cu-BHT active film
Measurement source: p005; article page 57239 · 3.3 Gas-Sensing Performance · Figure 3e,g

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Response retained after 2 months in air	within 90% of initial value after exposure to ambient air for 2 months	—	—	Text Approximate	p005; article page 57239 · 3.3 Gas-Sensing Performance · Figure 3g