A Novel Electrically Conductive Perylene Diimide-Based MOF-74 Series Featuring Luminescence and Redox Activity · Scheurle P.I., Biewald A., Mahringer A. et al. · Small Structures · 2022 · 2100195
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
PDI-MOF-74(Mg) powder · Powder
TGA from room temperature to 800 C under synthetic air, 25 mL/min, 1 K/min
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| first TGA weight loss | about 5% | — | — | Text Approximate | 4 · Results and Discussion · Figure S15 |
| thermal degradation threshold | no thermal degradation below 300 C | — | — | Text Approximate | 4 · Results and Discussion · Figure S15 |
PDI-MOF-74(Ni) powder · Powder
TGA from room temperature to 800 C under synthetic air, 25 mL/min, 1 K/min
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| first TGA weight loss | about 5% | — | — | Text Approximate | 4 · Results and Discussion · Figure S15 |
| thermal degradation threshold | no thermal degradation below 300 C | — | — | Text Approximate | 4 · Results and Discussion · Figure S15 |
PDI-MOF-74(Zn) powder · Powder
TGA from room temperature to 800 C under synthetic air, 25 mL/min, 1 K/min
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| first TGA weight loss | about 5% | — | — | Text Approximate | 4 · Results and Discussion · Figure S15 |
| thermal degradation threshold | no thermal degradation below 300 C | — | — | Text Approximate | 4 · Results and Discussion · Figure S15 |