Electrical Transport — Orientation Control of a Two-Dimensional Conductive Metal-Organic Framework Thin Film by a Pyridine Vapor-Assisted Dry Process

Measurement evidence

Electrical Transport

Orientation Control of a Two-Dimensional Conductive Metal-Organic Framework Thin Film by a Pyridine Vapor-Assisted Dry Process · Chon S., Nakayama R., Iwamoto S. et al. · ACS Applied Materials and Interfaces · 2023 · 56057-56063

2 measurement groups · 9 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

four-probe van der Pauw method using Keithley 2400 digital source meter

Electrical conductivity

(001)-oriented Cu3(HHTP)2 thin film annealed with 3 uL pyridine · Thin Film

Room-temperature in-plane conductivity; Au electrodes at four corners, 5 mm x 5 mm film specimen, electrode distance about 3 mm; currents 1.00 x 10^-8 to 5.00 x 10^-7 A.

Temperature
room temperature
Geometry
van der Pauw, Au corner electrodes on thin film
Context
pristine framework
Measurement source
p004 · Table S1 caption · Figure S4; Table S1
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
annealed conductivity at 1.00 x 10^-7 A2.6 x 10^-2 S cm^-1——SI Table
Rounded Reported		p004 · Table S1 · Table S1
annealed conductivity at 1.00 x 10^-8 AMarked as a best value within this paper2.6 x 10^-2 S cm^-1——SI Table
Rounded Reported		p004 · Table S1 · Table S1
annealed conductivity at 5.00 x 10^-7 A2.6 x 10^-2 S cm^-1——SI Table
Rounded Reported		p004 · Table S1 · Table S1
annealed conductivity at 5.00 x 10^-8 A2.6 x 10^-2 S cm^-1——SI Table
Rounded Reported		p004 · Table S1 · Table S1
conductivity current-independence indicates ohmic contactconstancy of conductivity over the entire current range indicates ohmic contact——Caption
Qualitative		p004 · Table caption · Table S1

four-probe van der Pauw method using Keithley 2400 digital source meter

Electrical conductivity

as-deposited Cu3(HHTP)2-like thin film on alpha-Al2O3 (001) · Thin Film

Room-temperature in-plane conductivity of noncrystalline as-deposited thin film; Au electrodes at four corners; currents 1.00 x 10^-8 to 5.00 x 10^-7 A.

Temperature
room temperature
Geometry
van der Pauw, Au corner electrodes on thin film
Context
pristine framework-like film
Measurement source
p004 · Table S1 caption · Figure S4; Table S1
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
as-deposited conductivity at 1.00 x 10^-7 A2.8 x 10^-2 S cm^-1——SI Table
Rounded Reported		p004 · Table S1 · Table S1
as-deposited conductivity at 1.00 x 10^-8 A2.6 x 10^-2 S cm^-1——SI Table
Rounded Reported		p004 · Table S1 · Table S1
as-deposited conductivity at 5.00 x 10^-7 A2.7 x 10^-2 S cm^-1——SI Table
Rounded Reported		p004 · Table S1 · Table S1
as-deposited conductivity at 5.00 x 10^-8 A2.7 x 10^-2 S cm^-1——SI Table
Rounded Reported		p004 · Table S1 · Table S1