Other — High performance metal–organic-framework coatings obtained via thermal gradient synthesis

Measurement evidence

Other

High performance metal–organic-framework coatings obtained via thermal gradient synthesis · Jeremias F., Henninger S.K., Janiak C. · Chemical Communications · 2012 · 9708-9710

1 measurement group · 4 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Coating thickness/area/growth rate from synthesis outcome

HKUST-1 coating on 5 cm x 5 cm copper sheet · Thin Film

Thermal-gradient growth from Cu(NO3)2-trimesic acid-DMF solution for 120 min on 5 cm x 5 cm Cu support.

Temperature: 423 K interface temperature in SI; main outcome text does not specify temperature in same sentence
Atmosphere: solution in stirred ice-water bath; atmosphere not specified
Geometry: 5 cm x 5 cm Cu sheet; coating on heated surface
Context: MOF coating on copper support with bottom interlayer
Measurement source: 9708-9709 · Abstract and Results

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
coated copper support area	25 cm2	—	—	Text Exact Reported	9709 · Results
coating thicknessMarked as a best value within this paper	100 um	—	—	Text Rounded Reported	9709 · Results
coating growth rateMarked as a best value within this paper	50 um h^-1	—	—	Text Rounded Reported	9708 · Abstract
preparation-to-preparation physical-property variance	within 3% from 6 preparations	—	from 6 preparations	Text Rounded Reported	9709 · Results