Other — Colossal Increase in Electric Current and High Rectification Ratio in a Photoconducting, Self-Cleaning, and Luminescent Schottky Barrier NMOF Diode

3 measurement groups · 12 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Drop-cast NMOF-1 film on glass · Thin Film

4 uL water droplets; at least ten static contact-angle measurements; self-cleaning test by rolling droplets

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
water contact angle upper bound	153-157 deg	—	—	Text Range	3 · Results and Discussion · Figure 1g
water contact angle lower bound	153-157 deg	—	—	Text Range	3 · Results and Discussion · Figure 1g
contact-angle hysteresis	~5 deg	—	—	Text Approximate	3 · Results and Discussion · Figure 1g
sliding angle upper bound	5-6 deg	—	—	Text Range	3 · Results and Discussion
sliding angle lower bound	5-6 deg	—	—	Text Range	3 · Results and Discussion

NMOF-1 bulk nanosheets/powder · Nanosheet

Elemental analysis of isolated NMOF-1 powder

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
calculated C content	C, 71.4	—	—	Text Exact Reported	10 · Synthesis of NMOF-1
found C content	C, 69.1	—	—	Text Exact Reported	10 · Synthesis of NMOF-1
calculated H content	H, 7.9	—	—	Text Exact Reported	10 · Synthesis of NMOF-1
found H content	H, 7.7	—	—	Text Exact Reported	10 · Synthesis of NMOF-1
molecular formula	Zn(OPE-C12).2H2O; elemental analysis calcd for C48H64O8Zn	—	—	Text Exact Reported	2 · Results and Discussion

NMOF-1 bulk nanosheets/powder · Nanosheet

Mettler Toledo TGA 850, 25-850 C, 3 C/min

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
thermal stability onset	stable up to 320 C	—	—	Text Exact Reported	2 · Results and Discussion · Figure S5
weight loss to 150 C	4.0% up to 150 C	—	—	Text Exact Reported	2 · Results and Discussion · Figure S5