Other — Electrochemical synthesis of metal organic framework films with proton conductive property

3 measurement groups · 15 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

as-prepared NENU-3 films on copper · Thin Film

Copper slice as anodic electrode at 2.0 V for 0.5-8 h.

Geometry: electrochemical synthesis solution
Context: synthesis solution for target framework
Measurement source: 4-5 · Table 2; Synthesis and characterizations · Table 2

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Cu2+ concentration at 2.0 V for 0.5 h	59.7 mg L-1	—	—	Table Exact Reported	4 · Table 2 · Table 2
Cu2+ concentration at 2.0 V for 1 h	117.0 mg L-1	—	—	Table Exact Reported	4 · Table 2 · Table 2
Cu2+ concentration at 2.0 V for 2 h	467.0 mg L-1	—	—	Table Exact Reported	4 · Table 2 · Table 2
Cu2+ concentration at 2.0 V for 4 h	1030.0 mg L-1	—	—	Table Exact Reported	4 · Table 2 · Table 2
Cu2+ concentration at 2.0 V for 6 h	1195.0 mg L-1	—	—	Table Exact Reported	4 · Table 2 · Table 2
Cu2+ concentration at 2.0 V for 8 h	1260.0 mg L-1	—	—	Table Exact Reported	4 · Table 2 · Table 2

as-prepared NENU-3 films on copper · Thin Film

Copper slice as anodic electrode at different applied voltages for 2 h.

Geometry: electrochemical synthesis solution
Context: synthesis solution for target framework
Measurement source: 3,5 · Table 1; Synthesis and characterizations · Table 1

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Cu2+ concentration at 1.0 V for 2 h	16.7 mg L-1	—	—	Table Exact Reported	3 · Table 1 · Table 1
Cu2+ concentration at 2.0 V for 2 h	467.0 mg L-1	—	—	Table Exact Reported	3 · Table 1 · Table 1
Cu2+ concentration at 5.0 V for 2 h	1220.0 mg L-1	—	—	Table Exact Reported	3 · Table 1 · Table 1
Cu2+ concentration at 8.0 V for 2 h	1545.0 mg L-1	—	—	Table Exact Reported	3 · Table 1 · Table 1

as-prepared NENU-3 films on copper · Thin Film

Thermal stability of NENU-3 material.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
decomposition complete	about 500 deg C	—	—	Text Approximate	6 · Stability · Fig. 6A
decomposition onset	around 285 deg C	—	—	Text Approximate	6 · Stability · Fig. 6A
first water-loss event	around 80 deg C	—	—	Text Approximate	6 · Stability · Fig. 6A
second water-loss event	around 120 deg C	—	—	Text Approximate	6 · Stability · Fig. 6A
thermal stability limit	up to 280 deg C	—	—	Text Rounded Reported	6 · Stability · Fig. 6A