Other — Ammonia-Assisted Chemical Vapor Deposition Growth of Two-Dimensional Conjugated Coordination Polymer Thin Films

4 measurement groups · 8 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Cu-BHT-w NH3-assisted CVD thin film · Thin Film

Mechanical property map comparing Cu-BHT-w with Fe-HHB-w, Cu-HHB-w and reported MOFs.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
elastic modulus	12.2 GPa	—	—	Text Exact Reported	SI p33 · Figure S29 discussion · Figure S29
hardness	~0.20 GPa	—	—	Text Approximate	SI p33 · Figure S29 discussion · Figure S29

Cu-HHB-w NH3-assisted CVD thin film · Thin Film

Mechanical property map comparing Cu-HHB-w with Fe-HHB-w, Cu-BHT-w and reported MOFs.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
elastic modulus	~34.1 GPa	—	—	Text Approximate	SI p33 · Figure S29 discussion · Figure S29
hardness	~0.69 GPa	—	—	Text Approximate	SI p33 · Figure S29 discussion · Figure S29

Fe-HHB-o CVD thin film without NH3 · Thin Film

Hysitron/Bruker TI950 TriboIndenter; Berkovich tip; peak load 65 uN for Fe-HHB-o; 16 indents.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
elastic modulus	~25.7 GPa	—	—	Text Approximate	18194 · Results and Discussion · Figure 5b
hardness	~0.9 GPa	—	—	Text Approximate	18194 · Results and Discussion · Figure 5c

Fe-HHB-w NH3-assisted CVD thin film · Thin Film

Hysitron/Bruker TI950 TriboIndenter; Berkovich tip; peak load 200 uN for Fe-HHB-w; 16 indents.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
elastic modulusMarked as a best value within this paper	~43.8 GPa	—	—	Text Approximate	18194 · Results and Discussion · Figure 5b
hardnessMarked as a best value within this paper	~2.0 GPa	—	—	Text Approximate	18194 · Results and Discussion · Figure 5c