Electrical Transport — Electrochemical Capacitance Traces with Interlayer Spacing in Two-dimensional Conductive Metal–Organic Frameworks

4 measurement groups · 4 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Bu-MOF pressed pellet · Pellet

Pressed pellets measured at room temperature under ambient atmosphere using Keithley 2450 source-meter and Keithley 2182A voltmeter.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
electrical conductivity	0.5 mS/cm	—	—	Text Rounded Reported	2 · Results · Figure 1d

Et-MOF pressed pellet · Pellet

Pressed pellets measured at room temperature under ambient atmosphere using Keithley 2450 source-meter and Keithley 2182A voltmeter.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
electrical conductivity	1.1 mS/cm	—	—	Text Rounded Reported	2 · Results · Figure 1d

H-MOF pressed pellet · Pellet

Pressed pellets measured at room temperature under ambient atmosphere using Keithley 2450 source-meter and Keithley 2182A voltmeter.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
electrical conductivity	1.9 mS/cm	—	—	Text Rounded Reported	2 · Results · Figure 1d

Pent-MOF pressed pellet · Pellet

Pressed pellets measured at room temperature under ambient atmosphere using Keithley 2450 source-meter and Keithley 2182A voltmeter.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
electrical conductivity	0.13 mS/cm	—	—	Text Rounded Reported	2 · Results · Figure 1d