Porosity — Electrochemical Capacitance Traces with Interlayer Spacing in Two-dimensional Conductive Metal–Organic Frameworks

4 measurement groups · 8 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Bu-MOF as-synthesised powder · Powder

N2 isotherms measured at 77 K; samples heated to 90 C under 0.3 mtorr vacuum for 16 h before analysis.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
apparent BET surface area	522 m2/g	—	—	Text Rounded Reported	2 · Results · Figure 1e; Figure S5
single point N2 desorption total pore volume	0.236 cm3/g	—	—	SI Table Exact Reported	11 · N2 sorption isotherms · Table S2

Et-MOF as-synthesised powder · Powder

N2 isotherms measured at 77 K; samples heated to 90 C under 0.3 mtorr vacuum for 16 h before analysis.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
apparent BET surface area	664 m2/g	—	—	Text Rounded Reported	2 · Results · Figure 1e; Figure S5
single point N2 desorption total pore volume	0.263 cm3/g	—	—	SI Table Exact Reported	11 · N2 sorption isotherms · Table S2

H-MOF as-synthesised powder · Powder

N2 isotherms measured at 77 K; samples heated to 90 C under 0.3 mtorr vacuum for 16 h before analysis.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
apparent BET surface area	735 m2/g	—	—	Text Rounded Reported	2 · Results · Figure 1e; Figure S5
single point N2 desorption total pore volume	0.353 cm3/g	—	—	SI Table Exact Reported	11 · N2 sorption isotherms · Table S2

Pent-MOF as-synthesised powder · Powder

N2 isotherms measured at 77 K; samples heated to 90 C under 0.3 mtorr vacuum for 16 h before analysis.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
apparent BET surface area	421 m2/g	—	—	Text Rounded Reported	2 · Results · Figure 1e; Figure S5
single point N2 desorption total pore volume	0.184 cm3/g	—	—	SI Table Exact Reported	11 · N2 sorption isotherms · Table S2