Porosity — Enhanced Electrical Conductivity by the Heavy Chalcogen Effect in Metal-Organic Frameworks

3 measurement groups · 6 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Cu-S-HHS solvothermal powder · Powder

Soaked in water 3 x 6 h, solvent exchange with acetone 3 x 6 h, vacuum dried room temperature 6 h, degassed at 80 C for 6 h; N2 at 77 K.

Temperature: 77
Context: pristine framework sample
Measurement source: S34-S35 · 11. Nitrogen adsorption isotherms · Figure S35

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Cu-S-HHS BET surface area	380 m2/g	—	—	Text Exact Reported	S34 · 11. Nitrogen adsorption isotherms · Figure S35
Cu-S-HHS pore-size distribution centre	13.0 Å	—	—	Text Exact Reported	S34 · 11. Nitrogen adsorption isotherms · Figure S35

Cu-Se-HHS solvothermal powder · Powder

Soaked in water 3 x 6 h, solvent exchange with acetone 3 x 6 h, vacuum dried room temperature 6 h, degassed at 80 C for 6 h; N2 at 77 K.

Temperature: 77
Context: pristine framework sample
Measurement source: S34-S35 · 11. Nitrogen adsorption isotherms · Figure S35

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Cu-Se-HHS BET surface area	435 m2/g	—	—	Text Exact Reported	S34 · 11. Nitrogen adsorption isotherms · Figure S35
Cu-Se-HHS pore-size distribution centre	13.0 Å	—	—	Text Exact Reported	S34 · 11. Nitrogen adsorption isotherms · Figure S35

Cu-Te-HHS solvothermal powder · Powder

Soaked in water 3 x 6 h, solvent exchange with acetone 3 x 6 h, vacuum dried room temperature 6 h, degassed at 80 C for 6 h; N2 at 77 K.

Temperature: 77
Context: pristine framework sample
Measurement source: S34-S35 · 11. Nitrogen adsorption isotherms · Figure S35

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Cu-Te-HHS BET surface area	437 m2/g	—	—	Text Exact Reported	S34 · 11. Nitrogen adsorption isotherms · Figure S35
Cu-Te-HHS pore-size distribution centre	13.5 Å	—	—	Text Exact Reported	S34 · 11. Nitrogen adsorption isotherms · Figure S35