Other — Redox-Active Mixed-Linker Metal–Organic Frameworks with Switchable Semiconductive Characteristics for Tailorable Chemiresistive Sensing

3 measurement groups · 13 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Mn2[TTF]x[NiS4]1-x powder series · Powder

Mn:Ni elemental ratios converted to linker ratios for mixed-linker formulas.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
ICP-AES assigned formula for Mn2[TTF]0.24[NiS4]0.76	Mn2[TTF]0.24[NiS4]0.76	—	—	SI Table Exact Reported	28 · Table S3 · Table S3
ICP-AES assigned formula for Mn2[TTF]0.49[NiS4]0.51	Mn2[TTF]0.49[NiS4]0.51	—	—	SI Table Exact Reported	28 · Table S3 · Table S3
ICP-AES assigned formula for Mn2[TTF]0.78[NiS4]0.22	Mn2[TTF]0.78[NiS4]0.22	—	—	SI Table Exact Reported	28 · Table S3 · Table S3
NiS4 linker fraction for Mn2[TTF]0.24[NiS4]0.76	0.76	—	—	SI Table Exact Reported	28 · Table S3 · Table S3
NiS4 linker fraction for Mn2[TTF]0.49[NiS4]0.51	0.51	—	—	SI Table Exact Reported	28 · Table S3 · Table S3
NiS4 linker fraction for Mn2[TTF]0.78[NiS4]0.22	0.22	—	—	SI Table Exact Reported	28 · Table S3 · Table S3
TTF linker fraction x for Mn2[TTF]0.24[NiS4]0.76	0.24	—	—	SI Table Exact Reported	28 · Table S3 · Table S3
TTF linker fraction x for Mn2[TTF]0.49[NiS4]0.51	0.49	—	—	SI Table Exact Reported	28 · Table S3 · Table S3
TTF linker fraction x for Mn2[TTF]0.78[NiS4]0.22	0.78	—	—	SI Table Exact Reported	28 · Table S3 · Table S3

Mn2[TTF]x[NiS4]1-x powder series · Powder

TGA 4000; 10 C min-1 under N2.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
thermal stability before framework collapse	up to 350 C	—	—	Text Rounded Reported	3 · Results and Discussion · Figure S12

Mn2[TTF]x[NiS4]1-x powder series · Powder

WCA measurements for Mn2[TTF], Mn2[TTF]0.49[NiS4]0.51, and Mn2[NiS4].

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
water contact angle of Mn2[NiS4]Marked as a best value within this paper	90.4 deg	—	—	Text Exact Reported	6 · Results and Discussion · Figure S33
water contact angle of Mn2[TTF]	71.6 deg	—	—	Text Exact Reported	6 · Results and Discussion · Figure S33
water contact angle of Mn2[TTF]0.49[NiS4]0.51	77.2 deg	—	—	Text Exact Reported	6 · Results and Discussion · Figure S33