Measurement evidence
Enhancing Near-Infrared Photothermal Performance by Molecular Aggregation Optimization in Semiconductive Coordination Polymers · Yan Y., Li Z.-Y., Qu K.-G. et al. · Inorganic Chemistry · 2024 · 22502-22511
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
compound 2 pure microcrystalline product · Powder
Compound 1 and 2 spectra compared under same conditions.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| relative EPR signal / NDI radical anion dopingMarked as a best value within this paper | compound 2 higher than compound 1 | — | — | Qualitative Qualitative | 22508 · 3.4 Semiconductive Properties · Figure S18 |
compound 1 pure bulk product from CdCl2 variant · Powder
4000-400 cm-1 range; baseline not deducted according to SI caption.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|
compound 1 pure bulk product from CdCl2 variant · Powder
Crystalline powder used without BaSO4 dilution.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| absorption tail wavelength | tail reaching only 810 nm | — | — | Text Rounded Reported | 22505 · 3.2 Optical Absorption · Figure S8a |
| experimental optical band gap | 1.53 eV | — | — | Text Rounded Reported | 22505 · 3.2 Optical Absorption · Figure 2b |
| visible shoulder absorption peak | 484 nm | — | — | Text Rounded Reported | 22505 · 3.2 Optical Absorption · Figure 2a |
compound 2 pure microcrystalline product · Powder
Crystalline powder used without BaSO4 dilution.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| absorption tail wavelengthMarked as a best value within this paper | long tail extending to 1000 nm | — | — | Text Rounded Reported | 22505 · 3.2 Optical Absorption · Figure S8b |
| experimental optical band gapMarked as a best value within this paper | 1.23 eV | — | — | Text Rounded Reported | 22505 · 3.2 Optical Absorption · Figure 2b |
| visible shoulder absorption peakMarked as a best value within this paper | 520 nm | — | — | Text Rounded Reported | 22505 · 3.2 Optical Absorption · Figure 2a |